PA66

PA66 A218 BK 21N SOLVAY SHANGHAI

278

Unit Price:US$ 4,923 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	80 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 4589-2	23 %
UL flame retardant rating	3.2 mm	UL 94	HB
	UL flame retardant rating	1.6 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	0.8 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ASTM D790	290 Mpa
Bending modulus	23°C	ISO 178	9500 Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	9800 Mpa
Tensile strain	Break, 23°C	ISO 527-2	3.0 %
tensile strength	Break, 23°C	ISO 527-2/1A	210 Mpa
Tensile modulus	23°C	ISO 527-2/1A	11400 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Suggested maximum moisture content			0.20 %
Temperature at the rear of the barrel			270 to 280 °C
Temperature in the middle of the barrel			275 to 285 °C
Temperature at the front of the material cylinder			280 to 290 °C
Mold temperature			70 to 100 °C

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	263 °C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	255 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.6 %
	Water absorption rate	Saturation, 23°C	ISO 62	5.4 %
	Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.75 %
Shrinkage rate	Flow	ISO 294-4	0.35 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.1 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1
Dissipation factor		IEC 60250	0.010
Relative permittivity		IEC 60250	3.70
Dielectric strength	2.00 mm	IEC 60243-1	34 KV/mm
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Surface resistivity		IEC 60093	6.0E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 A218 BK 21N SOLVAY SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet