PC LEXAN™ EXL1414 8R8D093 SABIC INNOVATIVE NANSHA
151
- Unit Price:US$ 3,401 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:23MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performance
- Application Areas:Home appliance components｜Electronic Applications｜Bottle cap
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 89 |
| R计秤 | ASTM D785 | 121 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 125 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 139 °C |
| 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 140 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| TD：23to80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| MD：23到80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| vicat | -- | ISO 306/B120 | 146 °C |
| -- | ISO 306/B50 | 145 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTM D648 | 124 °C |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 128 °C | |
| vicat | ASTM D152510 | 145 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| 0.8mm | IEC 60695-2-12 | 850 °C | |
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 875 °C |
| 3.0mm | IEC 60695-2-13 | 875 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| 23°C | ISO 180/1U | NoBreak | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| 23°C | ISO 179/1eA | 70 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 770 J/m |
| 23°C | ASTM D256 | 870 J/m | |
| -30°C | ISO 180/1A | 60 kJ/m² | |
| 23°C | ISO 180/1A | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 1MHz | ASTM D150 | 9.3E-03 |
| 100Hz | ASTM D150 | 1.2E-03 | |
| dielectric constant | 1MHz | ASTM D150 | 2.64 |
| 100Hz | ASTM D150 | 2.68 | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| dielectric strength | 0.800mm,inOil | ASTM D149 | 16 KV/mm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % | |
| density | ASTM D792 | 1.18 g/cm³ | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| TD：3.20mm | 内部方法 | 0.40-0.80 % | |
| density | ISO 1183 | 1.19 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | ISO 178 | 2250 Mpa | |
| 50.0mm跨距 | ASTM D790 | 2230 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| elongation | 断裂 | ASTM D638 | 98 % |
| tensile strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| 断裂 | ASTM D638 | 50.3 Mpa | |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 55.5 Mpa |
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| bending strength | ISO 178 | 85.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 92.4 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.