PEI

PEI ULTEM™ 2312EPR-1000 SABIC INNOVATIVE US

264

Unit Price:US$ 10,558 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
14.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Aging resistance｜High temperature resistance
Application Areas:household electrical appliances｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	25 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	25 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	330 J/m
	Suspended wall beam without notch impact strength	-30°C9	ISO 180/1U	25 kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C9	ISO 180/1U	25 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	15.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--3	ASTM D638	6480 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	5300 Mpa
tensile strength	Yield4	ASTM D638	94.0 Mpa
	tensile strength	Yield	ISO 527-2/5	80.0 Mpa
		tensile strength	Break4	ASTM D638	94.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	80.0 Mpa
elongation	Yield4	ASTM D638	2.0 %
	elongation	Yield	ISO 527-2/5	2.0 %
		elongation	Break4	ASTM D638	2.0 %
		elongation	elongation	Break	ISO 527-2/5	2.0 %
Bending modulus	50.0 mm Span5	ASTM D790	5580 Mpa
Bending modulus	Bending modulus	--6	ISO 178	5500 Mpa
bending strength	--6,7	ISO 178	145 Mpa
bending strength	bending strength	Yield, 50.0 mm Span5	ASTM D790	156 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			330 to 400 °C
Temperature in the middle of the barrel			340 to 400 °C
Temperature at the front of the material cylinder			345 to 400 °C
Spray nozzle temperature			345 to 400 °C
Processing (melt) temperature			350 to 400 °C
Mold temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	204 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	206 °C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Bf	204 °C
			Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	199 °C
				Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	202 °C
				Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	192 °C
Vicat softening temperature	--	ASTM D152510	216 °C
	Vicat softening temperature	--	ISO 306/B50	211 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	213 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 150°C	ASTM E831	3.2E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 150°C	ISO 11359-2	3.2E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 150°C	ASTM E831	3.5E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 150°C	ISO 11359-2	3.5E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.32 W/m/K

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	14 g/10 min
Melt Volume Flow Rate (MVR)	360°C/5.0 kg	ISO 1133	14.0 cm3/10min
Shrinkage rate	Flow 2	Internal Method	0.40 - 0.60 %
	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.60 %
	Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.90 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.50 %

Electrical performance	Test Method	Test Result
Arc resistance	ASTM D495	PLC 5
Compared to the anti leakage trace index	UL 746	PLC 4
High arc combustion index	UL 746	PLC 4
High voltage arc tracing rate	UL 746	PLC 4
Hot wire ignition	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ 2312EPR-1000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet