PC Makrolon® 2407 351308 COVESTRO SHANGHAI
190
- Unit Price:US$ 3,973 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low viscosity｜UV resistance｜High mobility｜Thermal stability｜Good demolding performance
- Application Areas:Industrial applications｜Electrical field｜Electronic field｜Automotive sector｜currency｜currency
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 116 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.58 °C | |
| transmittance | ISO 13468-2 | 89.0 % |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/Bf | 136 °C | |
| ISO 75-2/Af | 124 °C | ||
| vicat | ISO 306/B50 | 143 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 66.0 Mpa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 75 kJ/m² | |
| ISO 180/1A | 12 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 14 kJ/m² | |
| ISO 179/1eA | 65 kJ/m² | ||
| flexural modulus | ISO 178 | 2350 Mpa | |
| bending strength | ISO 178 | 98.0 Mpa | |
| Tensile creep modulus | ISO 899-1 | 1900 Mpa | |
| ISO 899-1 | 2200 Mpa | ||
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| Elongation at break | ISO 527-2 | >50 % |
| flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-2 0.75mm | |
| UL -94 | V-2 1.50mm | ||
| UL -94 | V-2 2.60mm | ||
| UL -94 | HB 2.70mm | ||
| UL -94 | HB 3.00mm | ||
| UL -94 | HB 6.00mm | ||
| Limiting Oxygen Index | ISO 4589-2 | 27 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | IEC 60250 | 3.00 1MHz | |
| Dissipation Factor | IEC 60250 | 5E-04 100HZ | |
| IEC 60250 | 9E-03 1MHz | ||
| IEC 60112 | 250 V | ||
| volume resistivity | IEC 60093 | 1E+15 Ω.cm | |
| Surface Resistivity | IEC 60093 | 1E+16 Ω.cm | |
| dielectric strength | IEC 60243-1 | 25 KV/mm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.2 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 19.0 cm3/10min | |
| shrinkage rate | ISO 294-4 | 0.70 % | |
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.12 % | ||
| shrinkage rate | ISO 294-4 | 0.65 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.