Plastic Raw Materials
PA66

PA66 Leona™  FG173 BK ASAHI JAPAN

270
  • Unit Price:US$ 4,392 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    100MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜Glass fiber content is 30% GF｜Flame retardant grade UL94 V-0
  • Application Areas:Hose｜Joint｜switch｜Electronic field｜Electrical field｜Electrical components｜Electrical/Electronic Applications｜switch｜Laptop case｜Joint｜switch｜Other electrical and electronic materials
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 17950 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
UL flame retardant rating0.75mmUL 94V-0
Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate湿0.6 %
mechanical propertiesTest ConditionTest MethodTest Result
Rockwell hardness干(湿)ASTM D-785100(60) M Scale
tensile strength干(湿)ASTM D-638167(142) Mpa
flexural coefficient干(湿)ASTM D-79010.8(8.3) GPa
Impact strength of cantilever beam gap干(湿)ASTM D-25688(98) J/m
Elongation at Break干(湿)ASTM D-6382.5(2.7) %
bending strength干(湿)ASTM D-790250(221) Mpa
Tensile strainBreak,23°CISO 527-22.0 %
Bending modulusASTM D79010800 Mpa
Bending modulus23°CISO 17810300 Mpa
bending strengthASTM D790250 Mpa
bending strength23°CISO 178259 Mpa
Taber abraser1000CyclesASTM D1044-- mg
Tensile modulus23°CISO 527-211700 Mpa
tensile strengthASTM D638167 Mpa
tensile strengthBreak,23°CISO 527-2174 Mpa
elongationBreakASTM D6382.5 %
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionMDASTM D6963E-05 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A245 °C
Hot deformation temperature1.8MPa,UnannealedASTM D648252 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B262 °C
Hot deformation temperature0.45MPa,UnannealedASTM D648260 °C
Linear coefficient of thermal expansion干ASTM D-6963
UL flame retardant rating干UL 94V-0
Hot deformation temperature0.46MPa,干ASTM D-648260 °C
Hot deformation temperature1.82MPa,干ASTM D-648252 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rate干旭化成方法0.3-0.7 %
Wear factor湿ASTM D-104429
Shrinkage rateTDInternal Method0.70 %
Shrinkage rateMDInternal Method0.30 %
Shrinkage rate吸水率(Saturation,23°C)Internal Method-- %
Water absorption rateEquilibrium,23°C,50%RHISO 62-- %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityASTM D2571E+14 ohms
Compared to the anti leakage trace index3.00mmIEC 60112 V
Dielectric strengthIEC 60243-128 KV/mm
Dielectric strengthASTM D14928 KV/mm
Surface resistivityIEC 600931E+14 ohms
Volume resistivityASTM D2571E+15 ohms·cm
Volume resistivity23°CIEC 600931E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM-ScaleISO 2039-2100
Rockwell hardnessM-ScaleASTM D785100
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.