PA66 A 218 W V30 SOLVAY KOREA

214

Unit Price:US$ 3,100 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Pipeline components｜Non specific food applications｜Electrical appliances
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	75 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D256	95.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	85 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	1.6mm	IEC 60695-2-12	700 °C
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ASTM D790	270 Mpa
Bending modulus	23°C	ISO 178	9000 Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	9000 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
elongation	Break,23°C	ASTM D638	3.5 %
tensile strength	Break,23°C	ISO 527-2/1A	190 Mpa
tensile strength	tensile strength	Yield,23°C	ASTM D638	190 Mpa
Tensile modulus	23°C	ISO 527-2/1A	10000 Mpa
bending strength	23°C	ISO 178	275 Mpa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	262 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	255 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	250 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	260 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ISO 62	0.80 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Dissipation factor		IEC 60250	0.020
Relative permittivity		IEC 60250	3.70
Dielectric strength	2.00mm	IEC 60243-1	35 KV/mm
Volume resistivity		IEC 60093	1E+15 ohms·cm
Surface resistivity		IEC 60093	1E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.