PC/PBT XENOY™ 1105-78211 SABIC INNOVATIVE SHANGHAI

234

Unit Price:US$ 3,194 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
53MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Chemical resistance｜Low temperature impact resistance
Application Areas:Household daily necessities｜Electrical applications｜Automotive Applications
Color:--
Grade:Impact resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
23°C		ISO 180/1A	63 kJ/m²
-30°C		ISO 180/1A	51 kJ/m²
-40°C18	-40℃	ISO 180/1A	35 kJ/m²
23°C		ASTM D256	760 J/m
0°C		ASTM D256	720 J/m
-10°C		ASTM D256	700 J/m
-20°C		ASTM D256	690 J/m
-30°C		ASTM D256	490 J/m
-40°C	-40℃	ASTM D256	370 J/m
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	48 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	63 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
--1		ASTM D638	1990 Mpa
--2		ASTM D638	2020 Mpa
crack		ASTM D638	110 %
yield		ISO 527-2/50	4.5 %
	yield		ASTM D638	4.2 %
	yield	yield		ASTM D638	4.1 %
crack		ISO 527-2/50	50.5 Mpa
	crack		ASTM D638	47.4 Mpa
	crack	crack		ASTM D638	46.0 Mpa
yield		ISO 527-2/50	52.4 Mpa
	yield		ASTM D638	48.8 Mpa
	yield	yield		ASTM D638	45.2 Mpa
crack		ASTM D638	120 %
crack	crack		ISO 527-2/50	120 %
50.0mm span		ASTM D790	1900 Mpa
--12		ISO 178	2020 Mpa
--13		ISO 178	78.9 Mpa
Yield, 50.0mm span		ASTM D790	76.1 Mpa
Fracture, 50.0mm span		ASTM D790	74.7 Mpa
Fracture bending strain		ISO 178	7.3 %

thermal performance	Test Method	Test Result
0.45MPa, unannealed, 6.40mm	ASTM D648	115 °C
0.45MPa, unannealed, 64.0mm span	ISO 75-2/Bf	109 °C
1.8MPa, unannealed, 6.40mm	ASTM D648	97.0 °C
1.8MPa, unannealed, 64.0mm span of	ISO 75-2/Af	90.2 °C
Vicat softening temperature	ASTMD1525	123 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:3.20mm	Internal Method	0.80-1.0 %
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	0.80-1.0 %
melt mass-flow rate	250°C/5.0kg	ASTMD1238	16 g/10min
Specific volume		ASTM D792	1.20 cm³/g

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ISO 868	79

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT XENOY™ 1105-78211 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet