ABS NP2H-AT BK LANXESS THAI
219
- Unit Price:US$ 2,355 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties: Anti static
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB 类别 |
| Vicat softening temperature | 50N:120K/h | ISO 306 | 94 °C |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 60° | 93 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.80Mpa | ISO 75 | - °C |
| density | ISO 1183 | 1.05 g/cm³ | |
| Hot deformation temperature | 0.45Mpa | ISO 75 | - °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at Break | 50mm/min | ISO 527 | 20 % |
| bending strength | 2mm/min 80×10×4 | ISO 178 | 68 Mpa |
| Tensile stress | 50mm/min，Yield | ISO 527 | 43 Mpa |
| tensile strength | 50mm/min | ISO 527 | 33 Mpa |
| Tensile modulus | 1mm/min | ISO 527 | 2400 Mpa |
| Bending modulus | 2mm/min 80×10×4 | ISO 178 | 2300 Mpa |
| Rockwell hardness | t=6.4mm | ISO 2039-2 | 111 R标尺 |
| melt mass-flow rate | 220℃；10kg | ISO 1133 | 37 g/10min |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 17 kJ/m² |
| -20℃ | ISO 180/1A | - kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.