ABS POLYLAC® PA-757K ZHANGZHOU CHIMEI
1010
- Unit Price:US$ 1,309 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:1059.1MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity｜High gloss｜Medium impact resistance
- Application Areas:Automotive Applications｜Household daily necessities｜Home appliance components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 116 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.6E-05 cm/cm/°C |
| Vicat softening temperature | -- | ISO 306/B50 | 100 °C |
| -- | ISO 306/A50 | 104 °C | |
| -- | ASTM D15257 | 105 °C | |
| Hot deformation temperature | 1.8MPa,Annealed | ISO 75-2/A | 98.0 °C |
| 1.8MPa,Annealed | ASTM D648 | 95.0 °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 83.0 °C | |
| 1.8MPa,Unannealed | ASTM D648 | 85.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| Melt Volume Flow Rate (MVR) | 220°C/10.0kg | ISO 1133 | 18.0 cm3/10min |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.6 g/10min |
| density | 23°C | ISO 1183 | 1.05 g/cm³ |
| --3 | ASTM D792 | 1.05 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | --6 | ISO 178 | 76.0 Mpa |
| --5 | ASTM D790 | 80.4 Mpa | |
| Bending modulus | --5 | ASTM D790 | 2620 Mpa |
| --6 | ISO 178 | 2200 Mpa | |
| elongation | Break | ISO 527-2/50 | 30 % |
| tensile strength | Yield4 | ASTM D638 | 45.9 Mpa |
| Yield | ISO 527-2/50 | 47.0 Mpa | |
| Break | ISO 527-2/50 | 34.0 Mpa | |
| elongation | Break4 | ASTM D638 | 25 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 19 kJ/m² |
| -30°C | ISO 180/1A | 9.0 kJ/m² | |
| 23°C,6.40mm | ASTM D256 | 200 J/m | |
| 23°C,3.20mm | ASTM D256 | 210 J/m | |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 21 kJ/m² |
| -30°C | ISO 179 | 10 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.