PC Makrolon® 3108 COVESTRO THAILAND

346

Unit Price:US$ 4,770 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high viscosity
Application Areas:Medical supplies｜Nursing supplies
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	1000μm	ISO 13468-2	89.0	%
	transmissivity	2000μm	ISO 13468-2	89.0	%
	transmissivity	transmissivity	3000μm	ISO 13468-2	88.0	%
Refractive index		ISO 489	1.587
transmissivity	4000μm	ISO 13468-2	87.0	%
turbidity	3000μm	ISO 14782	<0.80	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6500	N
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	70.0	J
Impact strength of cantilever beam gap	23°C,Partial Break	ISO 180/A	90	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 180/A	16	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C,Partial Break	ISO 7391	80	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C,Complete Break	ISO 7391	18	kJ/m²
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5600	N
flammability	Test Condition	Test Method	Test Result	Test Unit
FlashIgnitionTemperature		ASTM D1929	480	°C
SelfIgnition		ASTM D1929	550	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1	2350	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	65.0	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	75.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	6.3	%
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	120	%
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50	%
Tensile creep modulus	1hr	ISO 899-1	2200	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1900	Mpa
Bending modulus	23°C	ISO 178	2350	Mpa
bending strength	3.5%Strain,23°C	ISO 178	72.0	Mpa
bending strength	bending strength	23°C	ISO 178	96.0	Mpa
Bending strain	23°C	ISO 178	7.2	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Ball Pressure Test	140°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B120	150	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	149	°C
Glass transition temperature		ISO 11357-2	149	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	129	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	141	°C
thermal conductivity	23°C	ISO 8302	0.20	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ISO 2577	0.60-0.80	%
Shrinkage rate	Shrinkage rate	TD	ISO 2577	0.60-0.80	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	6.00	cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	6.5	g/10min
Shrinkage rate	MD:2.00mm3	ISO 294-4	0.70	%
Shrinkage rate	Shrinkage rate	TD:2.00mm3	ISO 294-4	0.75	%
Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12	%
density	23°C	ISO 1183	1.20	g/cm³
Apparent density		ISO 60	0.66	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	111	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Jufengde	US$ 4550 /MT

Supplier Join

Get App

Top

PC Makrolon® 3108 COVESTRO THAILAND

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index