ABS POLYLAC® PA-707K ZHENJIANG CHIMEI
422
- Unit Price:US$ 1,293 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:39MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity｜High gloss
- Application Areas:Office supplies｜Lighting fixtures｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning rate | 1/16" | File NO.E196075 | HB |
| Hot deformation temperature | Annealed（Unannealed） | ASTM D-648 | 99(210)/88(190) ℃(°F) |
| Vicat softening temperature | ASTM D-1525 | 105(221) ℃(°F) | |
| ASTM D1525/ISO R306 | 105(221) ℃（℉） | ||
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 88(190) ℃（℉） |
| HDT | ASTM D648/ISO 75 | 99(210) ℃（℉） | |
| Combustibility (rate) | UL 94 | 1/16"HB |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 高光泽性 高刚性 |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 200℃ 10kg | ISO 1133 | 23 g/10min |
| 200℃ 5kg | ASTM D-1238 | 1.9 g/10min |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 23 g/10min | |
| ASTM D1238/ISO 1133 | 1.9 g/10min | ||
| density | ASTM D792/ISO 1183 | 1.06(1.9) |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ASTM D-790 | 860 kg/cm2 | |
| Bending modulus | ASTM D-790 | 2.9 104kg/cm2 | |
| Rockwell hardness | ASTM D-785 | 116 R | |
| tensile strength | ASTM D-638 | 500 kg/cm2 | |
| Impact strength of cantilever beam gap | 1/4〃(1/8") | ASTM D-256 | 14(15) kg.cm/cm |
| Elongation at Break | ASTM D-638 | 15 % | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 15(2.7) kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 860（12.200） kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 29000（41000） kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | R-116 | |
| elongation | ASTM D638/ISO 527 | 15 % | |
| tensile strength | ASTM D638/ISO 527 | 500（7.090） kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 14(2.6) kg·cm/cm(J/M)ft·lb/in |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.