Material Description
- Material Properties:High impact resistance｜heat-resisting
- Application Areas:Electrical field｜Electronic field｜Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 129 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 130 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 113 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 110 °C | |
| vicat | ISO 306/B50 | 130 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| RTI Elec | UL 746 | 105 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Str | UL 746 | 105 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.2mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 34 kJ/m² |
| 23°C | ISO 180/1A | 49 kJ/m² | |
| Dart impact | -30°C,TotalEnergy | ASTM D3763 | 54.2 J |
| 23°C,TotalEnergy | ASTM D3763 | 54.2 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 19 g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 24.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2280 Mpa | |
| ISO 527-2/1 | 2370 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 57.2 Mpa |
| 屈服 | ISO 527-2/50 | 55.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.8 % |
| elongation | 断裂 | ASTM D638 | 150 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| ISO 178 | 2250 Mpa | ||
| bending strength | ISO 178 | 86.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 88.3 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.