PC/PBT Makroblend® KU2-7912/4 BK COVESTRO GERMANY
311
- Unit Price:US$ 3,212 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:36MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:wear resistant｜High elasticity｜Fast forming cycle
- Application Areas:shoes｜film｜Stationery
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 100 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 106 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 82.0 °C | |
| vicat | ISO 306/B120 | 125 °C | |
| melting temperature | ISO 11357-3 | 223 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 700 °C |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| Burning rate - US-FMVSS | >1.00mm | ISO 3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| electrolytic corrosion | 23°C | IEC 60426 | A1 |
| GottfertMeltViscosity | 260°C | 内部方法 | 670 Pa·s |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 60 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180 | NoBreak |
| 23°C | ISO 180 | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
| 23°C | ISO 179/1eA | 60 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 45 kJ/m² |
| -20°C | ISO 180/A | 52 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+17 ohms | |
| volume resistivity | 23°C | IEC 60093 | >1.0E+17 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.20 |
| 23°C,1MHz | IEC 60250 | 3.10 | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 1.5E-03 |
| 23°C,1MHz | IEC 60250 | 0.013 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
| 解决方案B | IEC 60112 | PLC 4 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Apparent density | ISO 60 | 0.70 g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 16.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | 23°C | ISO 178 | 2100 Mpa |
| bending strength | 23°C | ISO 178 | 75.0 Mpa |
| 3.5%Strain,23°C | ISO 178 | 66.0 Mpa | |
| Bending Strain | 23°C | ISO 178 | 5.5 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2150 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 50.0 Mpa |
| 断裂,23°C | ISO 527-2/50 | 45.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 4.0 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.