ABS

ABS POLYLAC® PA-758R TAIWAN CHIMEI

459

Unit Price:US$ 2,391 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
346.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜transparent｜Chemical resistance
Application Areas:Monitor｜small home appliances｜Electronic field｜Electrical field
Color:--
Grade:Transparent level

Material Certification

MSDS

RoHS

MSDS

TDS

MSDS

RoHS

SVHC

Processing

Statement

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	14 kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	160 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	150 J/m
Charpy Notched Impact Strength	23°C	ISO 179	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	7.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break3	ASTM D638	40 %
elongation	elongation	Break	ISO 527-2/50	40 %
Bending modulus	--4	ASTM D790	1900 Mpa
Bending modulus	Bending modulus	--5	ISO 178	1900 Mpa
tensile strength	--3	ASTM D638	39.7 Mpa
	tensile strength	Break	ISO 527-2/50	33.0 Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/50	42.0 Mpa
bending strength	--5	ISO 178	57.0 Mpa
bending strength	bending strength	--4	ASTM D790	53.9 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	99.0 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	77.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	88.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	96.0 °C
	Vicat softening temperature	--	ISO 306/A50	104 °C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15256	105 °C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	97.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	0.30-0.70 %
melt mass-flow rate	200°C/5.0kg	ASTMD1238	3.0 g/10min
density	23°C	ISO 1183	1.08 g/cm³
density	density	--	ASTM D792	1.08 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	107

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS POLYLAC® PA-758R TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet