PBT

PBT VALOX™ 357 1001 SABIC INNOVATIVE SHANGHAI

358

Unit Price:US$ 4,549 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
115MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜UV resistance
Application Areas:Electrical appliances｜Plastic bag｜Casters｜Household goods｜Spool｜Shell｜switch
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	45 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	150 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	320 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	35.8 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	45 kJ/m²
Dart impact	23°C	ASTM D3029	43.4 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	NoBreak
Dart impact	23°C11	ASTM D3029	43.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.46mm	UL 94	HB
	UL flame retardant rating	0.63mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	775 °C
	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	750 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725 °C
Extreme Oxygen Index		ASTM D2863	30 %

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	78.0 Mpa
bending strength	bending strength		ISO 178	73.0 Mpa
Bending modulus		ISO 178	2000 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2100 Mpa
Tensile strain	Yield	ISO 527-2/50	5.0 %
Tensile strain	Tensile strain	Yield	ASTM D638	5.0 %
tensile strength	Break	ISO 527-2/50	40.0 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	78.0 Mpa
Tensile strain	Break	ISO 527-2/50	30 %
Tensile strain	Tensile strain	Break	ASTM D638	54 %
tensile strength	Yield	ISO 527-2/50	50.0 Mpa
tensile strength	tensile strength	Break	ASTM D638	42.0 Mpa
Tensile modulus		ASTM D638	2020 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2200 Mpa
tensile strength	Yield	ASTM D638	48.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Elec		UL 746	120 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	8.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.2E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	145 °C
Vicat softening temperature	Vicat softening temperature		ASTM D152513	134 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	84.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	99.0 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	98.0 °C
			Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	138 °C
			Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	135 °C
Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.2E-05 cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B120	150 °C
RTI Imp		UL 746	120 °C
RTI Str		UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/5.0kg	ASTM D1238	9.6 g/10min
Shrinkage rate	TD：--3	Internal Method	1.2-1.6 %
Water absorption rate	24hr	ASTM D570	0.080 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.50 %
density		ASTM D792	1.35 g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Outdoor applicability		UL 746C	f2
Specific volume		ASTM D792	0.740 cm³/g
density		ISO 1183	1.34 g/cm³
Shrinkage rate	TD：--2	Internal Method	0.90-1.3 %
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	8.00 cm3/10min
Shrinkage rate	MD：--2	Internal Method	0.80-1.1 %
	Shrinkage rate	MD：--3	Internal Method	1.0-1.4 %
	Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	1.0-1.4 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	>1.2E+16 ohms·cm
Dielectric strength	1.60mm,in Oil	ASTM D149	25 KV/mm
Dielectric strength	Dielectric strength	3.20mm,inAir	ASTM D149	19 KV/mm
Dielectric constant	1MHz	ASTM D150	3.20
Dielectric strength	3.20mm,in Oil	ASTM D149	19 KV/mm
Dielectric constant	100Hz	ASTM D150	3.20
Dissipation factor	100Hz	ASTM D150	3E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.030
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	117

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT VALOX™ 357 1001 SABIC INNOVATIVE SHANGHAI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet