Other performance	Test Condition	Test Method	Test Result	Test Unit
Thickness Tested		UL 94	0.75	mm
Grade @ Thickness		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	3.2mm	ASTM D-638	135	Mpa
Impact strength of cantilever beam gap	3.2mm	ASTM D-256	80	J/m
Bending modulus	3.2mm	ASTM D-790	15600	Mpa
Elongation at Break	3.2mm	ASTM D-638	1.3	%
bending strength	3.2mm	ASTM D-790	182	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec	1.5mm	UL 746-B	240	°C
RTI Imp	0.8mm	UL 746-B	130	°C
Glass transition temperature		ASTM D-3418	120	°C
Melting temperature		ASTM D-3418	335	°C
RTI Imp	1.5mm	UL 746-B	210	°C
Hot deformation temperature	1.80MPa	ASTM D-648	271	°C
Chain melting temperature			350-360	°C
RTI Imp	3.0MPa	UL 746-B	220	°C
RTI Imp	RTI Imp	0.8mm	UL 746-B	240	°C
Temperature range for molding			30-95	°C
RTI Elec	0.8mm	UL 746-B	240	°C
drying temperature			135	°C
RTI Imp	1.5mm	UL 746-B	240	°C
RTI Imp	RTI Imp	3.0mm	UL 746-B	240	°C
RTI Elec	3.0mm	UL 746-B	240	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.