PC LEXAN™ EXL1433T SABIC INNOVATIVE US

238

Unit Price:US$ 5,500 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
51MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Middle flow｜High ductility at low temperature｜Short molding cycle
Application Areas:Automotive sector｜Electronic and Electrical Applications｜Plastic bag
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	2540μm	ASTM D1003	82.0	%
turbidity	2540μm	ASTM D1003	3.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	82.4	J
Dart impact	Dart impact	-30°C,TotalEnergy	ASTM D3763	85.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	50	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	70	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	45	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	65	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
23°C		ISO 180/1A	65	kJ/m²
-30°C		ISO 180/1A	45	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	50	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	70	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
-30°C		ASTM D256	800	J/m
23°C		ASTM D256	890	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	825	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	825	°C
UL flame retardant rating	2.5mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-2
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.800mm	IEC 60695-2-13	825	°C
UL flame retardant rating	2.50mm	UL 94	V-2
Burning wire flammability index	3.00mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	3.00mm	IEC 60695-2-13	825	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2220	Mpa
Bending modulus	50.0mmSpan	ASTM D790	2220	Mpa
Tensile strain	Break	ISO 527-2/50	120	%
elongation	Break	ASTM D638	130	%
Tensile strain	Yield	ISO 527-2/50	5.5	%
elongation	Yield	ASTM D638	5.8	%
tensile strength	Break	ISO 527-2/50	61.5	Mpa
	tensile strength	Break	ASTM D638	64.1	Mpa
		tensile strength	Yield	ISO 527-2/50	57.9	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	58.0	Mpa
Tensile modulus		ISO 527-2/1	2350	Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	94.3	Mpa
bending strength	bending strength		ISO 178	90.2	Mpa
Bending modulus		ISO 178	2150	Mpa
--1		ASTM D638	2220	Mpa
50.0mm span		ASTM D790	2220	Mpa
--7		ISO 178	2150	Mpa
--8		ISO 178	90.2	Mpa
Yield, 50.0mm span		ASTM D790	94.3	Mpa
yield		ASTM D638	58.0	Mpa
yield	yield		ISO 527-2/50	57.9	Mpa
crack		ASTM D638	64.1	Mpa
crack	crack		ISO 527-2/50	61.5	Mpa
yield		ASTM D638	5.8	%
yield	yield		ISO 527-2/50	5.5	%
crack		ASTM D638	130	%
crack	crack		ISO 527-2/50	120	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	119	°C
Vicat softening temperature		ASTM D152510	141	°C
	Vicat softening temperature	--	ISO 306/B50	141	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	142	°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124	°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to95°C	ASTME831	7.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	7.2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to95°C	ASTME831	7.9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	7.9E-05	cm/cm/°C
RTI Elec		UL 746	130	°C
RTI Str		UL 746	130	°C
1.8MPa, unannealed, 3.20mm		ASTM D648	124	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	119	°C
Flow: -40 to 95 ° C	-40to95℃	ASTME831	7.2E-05	cm/cm/°C
Flow: 23 to 80 ° C	23to80℃	ISO 11359-2	7.2E-05	cm/cm/°C
Horizontal: -40 to 95 ° C	Across Flow, -40to95℃	ASTME831	7.9E-05	cm/cm/°C
Horizontal: 23 to 80 ° C	Across Flow, 23to80℃	ISO 11359-2	7.9E-05	cm/cm/°C
RTI		UL 746	130	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.093	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.12	%
Shrinkage rate	TD：3.20mm	Internal Method	0.40-0.80	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.80	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.50	cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10	g/10min
Shrinkage rate	MD:3.20mm	Internal Method	0.40-0.80	%
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	>1.0E+15	ohms
Volume resistivity		ASTM D257	>1.0E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L-Sale	ASTM D785	90
Rockwell hardness	Rockwell hardness	L-Sale	ISO 2039-2	90

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC LEXAN™ EXL1433T SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index