PBT VALOX™ V4860HR BK1066 SABIC INNOVATIVE JAPAN
225
- Unit Price:US$ 7,953 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:21MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Dimensional stability
- Application Areas:Automotive Applications｜Casters
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.64 g/cm³ | |
| ISO 1183 | 1.64 g/cm³ | ||
| Water absorption rate | ISO 62 | 0.060 % | |
| ISO 62 | 0.19 % | ||
| Shrinkage rate | 内部方法 | 0.50-1.0 % | |
| 内部方法 | 0.50-0.70 % | ||
| Melt volume flow rate | ISO 1133 | 12.4 cm3/10min | |
| melt mass-flow rate | ASTM D1238 | 18 g/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ASTM D790 | 174 Mpa | |
| ASTM D790 | 2.96 Mpa | ||
| Fracture bending strain | ISO 178 | 2.9 % | |
| tensile strength | ISO 527-2/5 | 111 Mpa | |
| elongation | ASTM D638 | 2.3 % | |
| Tensile strain | ISO 527-2/5 | 2.1 % | |
| elongation | ASTM D638 | 2.3 % | |
| Tensile strain | ISO 527-2/5 | 2.2 % | |
| Flexural modulus | ASTM D790 | 6740 Mpa | |
| ISO 178 | 7880 Mpa | ||
| bending strength | ISO 178 | 182 Mpa | |
| ISO 178 | 183 Mpa | ||
| tensile strength | ASTM D638 | 115 Mpa | |
| ISO 527-2/5 | 112 Mpa | ||
| ASTM D638 | 116 Mpa | ||
| Tensile modulus | ISO 527-2/1 | 9450 Mpa | |
| ASTM D638 | 9750 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 11 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 74 J/m | |
| ASTM D256 | 90 J/m | ||
| ISO 180/1A | 8.5 kJ/m² | ||
| ISO 180/1A | 10 kJ/m² | ||
| Dart impact | ASTM D3763 | 13.4 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 197 °C | |
| ASTM D648 | 205 °C | ||
| ISO 75-2/Af | 188 °C | ||
| vicat | ASTM D152512 | 176 °C | |
| ISO 306/B50 | 176 °C | ||
| ISO 306/B120 | 175 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 2.4E-05 cm/cm/°C | |
| ISO 11359-2 | 2.3E-05 cm/cm/°C | ||
| ASTME831 | 1.1E-04 cm/cm/°C | ||
| ISO 11359-2 | 1.2E-04 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 221 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.