PC LEXAN™ 123R-111 SABIC EU

283

Unit Price:US$ 1,913 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Low viscosity｜High temperature resistance
Application Areas:Electronic and electrical components｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ISO 489	1.586
transmissivity	2540 μm	ASTM D1003	88.0 to 90.0 %
turbidity	2540 μm	ASTM D1003	< 0.80 %

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Impact strength of cantilever beam gap	23°C	ISO 180/1A	65 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0 mm	UL 94	HB
Burning wire flammability index	1.0 mm	IEC 60695-2-12	850 °C
UL flame retardant rating	0.75 mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	25 %

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	2300 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	10.0 mg
bending strength		ISO 178	90.0 Mpa
Tensile strain	Break	ISO 527-2/50	100 %
Tensile modulus		ISO 527-2/1	2350 Mpa
tensile strength	Break	ISO 527-2/50	65.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	63.0 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %

injection	Test Condition	Test Method	Test Result
Temperature at the rear of the barrel			260 to 280 °C
Temperature in the middle of the barrel			270 to 290 °C
Temperature at the front of the material cylinder			280 to 300 °C
Mold temperature			80 to 100 °C
Processing (melt) temperature			280 to 300 °C
Spray nozzle temperature			270 to 290 °C
Suggested maximum moisture content			0.020 %
Hopper temperature			60 to 80 °C
drying temperature			120 °C
drying time			2.0 to 4.0 hr

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	130 °C
Vicat softening temperature	--	ISO 306/B120	141 °C
RTI Imp		UL 746	130 °C
RTI Elec		UL 746	130 °C
Ball Pressure Test	140°C8	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
thermal conductivity		ISO 8302	0.20 W/m/K
Linear coefficient of thermal expansion	23 to 80°C，Flow	ISO 11359-2	7.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	140 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	122 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	133 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f1
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	21.0 cm3/10min
Shrinkage rate	Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	Saturation, 23°C	ISO 62	0.35 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17 KV/mm
Relative permittivity	50 Hz	IEC 60250	2.70
Relative permittivity	Relative permittivity	60 Hz	IEC 60250	2.70
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Dissipation factor	60 Hz	IEC 60250	1.0E-3
Dissipation factor	Dissipation factor	50 Hz	IEC 60250	1.0E-3
Relative permittivity	1 MHz	IEC 60250	2.70
Dissipation factor	1 MHz	IEC 60250	0.010

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H 358/30	ISO 2039-1	95.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top