PA66

PA66 TECHNYL® A 246 M SOLVAY FRANCE

328

Unit Price:US$ 4,909 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
80.9MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:Application in the automotive field｜sporting goods
Color:--
Grade:Toughened grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	97 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	16 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	23°C	ASTM D256	100 J/m
	Impact strength of cantilever beam gap	-30°C	ISO 180	22 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	60 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	25 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1A	1900 Mpa
tensile strength	Yield,23°C	ASTM D638	50.0 Mpa
	tensile strength	Yield,23°C	ISO 527-2/1A	47.0 Mpa
	tensile strength	tensile strength	Break,23°C	ISO 527-2/1A	44.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	20 %
elongation	Break,23°C	ASTM D638	80 %
Bending modulus	23°C	ASTM D790	1800 Mpa
Bending modulus	Bending modulus	23°C	ISO 178	1800 Mpa
bending strength	23°C	ASTM D790	70.0 Mpa
bending strength	bending strength	23°C	ISO 178	70.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	200 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	63.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	65.0 °C
Melting temperature		ASTM D3417	263 °C
Melting temperature	Melting temperature		ISO 11357-3	263 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183/A	1.08 g/cm³
Water absorption rate	23°C,24hr	ISO 62	1.1 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+15 ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dielectric strength	2.00mm	IEC 60243-1	30 KV/mm
Relative permittivity		IEC 60250	3.20
Dissipation factor		IEC 60250	0.020
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 TECHNYL® A 246 M SOLVAY FRANCE

Material Description

Technical Data Sheet Compare

Technical Data Sheet