MABS

MABS TR557 LG CHEM KOREA

425

Unit Price:US$ 2,579 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Material Certification

RoHS

MSDS

TDS

REACH

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	3200 μm, Injection	ASTM D1003	90.0 %
turbidity	Injection	ASTM D1003	2.0 %
Transmittance rate	Rate B/50	ASTM D1003	90 %
turbidity	-40°C to	ASTM D1003	2 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.2mm，23℃	ASTM D256	17 kg·cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	6.4mm，23℃	ASTM D256	17 kg·cm/cm

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C, 3.20 mm, Injection	ASTM D638	2050 Mpa
tensile strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	48.0 Mpa
elongation	Yield, 23°C, 3.20 mm, Injection	ASTM D638	> 5.0 %
elongation	elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	15 %
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	2250 Mpa
bending strength	23°C, 3.20 mm, Injection	ASTM D790	71.0 Mpa
tensile strength	3.2mm, 5，Yield	ASTM D638	470 kg/cm2
Elongation at Break	3.2mm, 5	ASTM D638	30 %
bending strength	3.2mm, 1	ASTM D790	700 kg/cm2
Bending modulus	3.2mm, 1	ASTM D790	22000 kg/cm2

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Temperature at the rear of the barrel			180 to 200 °C
Temperature in the middle of the barrel			190 to 210 °C
Temperature at the front of the material cylinder			200 to 220 °C
Spray nozzle temperature			190 to 220 °C
Processing (melt) temperature			190 to 220 °C
Mold temperature			40 to 60 °C
Back pressure			29.4 to 58.8 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	81.0 °C
Vicat softening temperature		ASTM D15257	89.0 °C
RTI Elec		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI		UL 746	50.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	21 g/10 min
Shrinkage rate	23°C, 3.20 mm, Injection，Flow	ASTM D955	0.40 - 0.70 %
melt mass-flow rate	/，220℃/10 kg	ASTM D 1238	20.621 g/10 min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	107
Hardness (Rockwell R)		ASTM D785	107 R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

MABS TR557 LG CHEM KOREA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet