Material Description

Material Properties:Glass fiber reinforced｜High temperature resistance
Application Areas:Automotive Applications｜Electrical applications
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	42	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	42	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	0.38 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	255	Mpa
Bending modulus	23°C	ISO 178	12000	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.9	%
tensile strength	Break	ISO 527-2/1A/5	165	Mpa
Tensile modulus		ISO 527-2/1A	12200	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Hopper temperature			20 to 30	°C
Temperature at the rear of the barrel			290 to 300	°C
Suggested maximum moisture content			0.020	%
drying time			3.0 to 4.0	hr
drying temperature			100 to 110	°C
Temperature in the middle of the barrel			310 to 320	°C
Temperature at the front of the material cylinder			330 to 340	°C
Spray nozzle temperature			310 to 330	°C
Processing (melt) temperature			330 to 340	°C
Mold temperature			140 to 160	°C
Injection speed			快速
Back pressure			< 3.00	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.2E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.9E-5	cm/cm/°C
Melting temperature		ISO 11357-3	280	°C
Glass transition temperature		ISO 11357-2	90.0	°C
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	205	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	265	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation, 23°C	ISO 62	0.020	%
Shrinkage rate	Flow	ISO 294-4	0.30 - 0.70	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.50 - 0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Surface resistivity		IEC 60093	> 1.0E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M -Sale	ISO 2039-2	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Zhifei	US$ 3650 /MT
Dongguan Yufeng	US$ 8820 /MT

Supplier Join

Get App

Top

PPS FORTRON® 1131L4 CELANESE USA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index