PA66 Zytel® 70G25HSLR NC010 DUPONT SHENZHEN

489

Unit Price:US$ 4,050 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
134.5MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜High temperature resistance
Application Areas:Bottle cap｜Automotive Applications｜Electrical applications
Color:--
Grade:Enhanced level

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt density			1.15	g/cm³
Top out temperature			210	°C
Specific Heat Capacity of Melt			2090	J/kg/°C
Thermal Conductivity of Melt			0.21	W/m/K
Odor		VDA 270	3.50
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00 mm	ISO 3795	26	mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
FMVSS combustion rate		FMVSS 302	B
雾化 - G-value (condensate)		ISO 6452	5.0E-4	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	260	Mpa
Bending modulus		ISO 178	8000	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	180	Mpa
Tensile modulus		ISO 527-2	8500	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			285 to 305	°C
Melt Temperature, Optimum			295	°C
Mold temperature			70 to 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 to 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	3.3E-5	cm/cm/°C
Melting temperature		ISO 11357-3	262	°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	261	°C
Vicat softening temperature		ISO 306/B50	257	°C
Glass transition temperature		ISO 11357-2	80.0	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	252	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	1.1	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30	%
Flow Length	2.00 mm		350	mm
Stickiness		ISO 307	150	cm³/g
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0	%
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.4	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 1
Dissipation factor	100 Hz	IEC 62631-2-1	7.0E-3
Relative permittivity	100 Hz	IEC 62631-2-1	3.60
Volume resistivity		IEC 62631-3-1	1.0E+13	ohms·m
Surface resistivity		IEC 62631-3-2	--	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H 961/30	ISO 2039-1	260	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 Zytel® 70G25HSLR NC010 DUPONT SHENZHEN

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index