PC/ABS Bayblend® FR3013 901510 COVESTRO GERMANY
174
- Unit Price:US$ 2,164 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Impact modification
- Application Areas:Household appliances｜Electronic field｜Electrical field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 86.0 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 78.0 °C | |
| vicat | -- | ISO 306/B50 | 89.0 °C |
| -- | ISO 306/B120 | 95.0 °C | |
| Linear coefficient of thermal expansion | 流动 : 23 到 55°C | ISO 11359-2 | 7.5E-5 cm/cm/°C |
| 横向 : 23 到 55°C | ISO 11359-2 | 7.6E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 5VB |
| Limiting Oxygen Index | ISO 4589-2 | 31 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 无断裂 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 240°C | ISO 11443-A | 155 Pa·s |
| ISO 9660 | PC+ABS-FR(40) |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 240°C/5.0 kg | ISO 1133 | 26.0 cm3/10min |
| shrinkage rate | 2.00 mm3 | ISO 294-4 | 0.40 - 0.60 % |
| 3.00 mm4 | ISO 2577 | 0.40 - 0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 5.0E+17 ohms | |
| volume resistivity | 23°C | IEC 60093 | 2.0E+18 ohms·cm |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80 °C | ||
| Drying time - Dry Air Dryer | 4.0 hr | ||
| Suggested maximum moisture content | < 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 220 to 230 °C | ||
| Temperature in the middle of the barrel | 225 to 235 °C | ||
| Temperature at the front of the material cylinder | 230 to 240 °C | ||
| Spray nozzle temperature | 255 to 265 °C | ||
| Processing (melt) temperature | 240 to 270 °C | ||
| mold temperature | 60 to 90 °C | ||
| Back pressure | 5.00 to 15.0 Mpa | ||
| Exhaust hole depth | 0.025 to 0.075 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2650 Mpa |
| tensile strength | 屈服, 23°C | ISO 527-2/50 | 61.0 Mpa |
| 断裂, 23°C | ISO 527-2/50 | 44.0 Mpa | |
| Tensile strain | 屈服, 23°C | ISO 527-2/50 | 4.0 % |
| 断裂, 23°C | ISO 527-2/50 | 30 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.