PPO/PA

PPO/PA NORYL GTX™ GTX4610-1710 SABIC INNOVATIVE US

401

Unit Price:US$ 5,821 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
110MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Hydrolysis resistance｜High temperature resistance｜Dimensional stability｜High mobility
Application Areas:Industrial machinery｜Electrical applications
Color:--
Grade:Flame retardant and high temperature resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	12.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	2.0mm	UL 94	5VB5VA
Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/5	88.0 Mpa
	tensile strength	Break4	ASTM D638	88.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/5	88.0 Mpa
Tensile strain	Yield	ISO 527-2/5	3.0 %
Tensile strain	Tensile strain	Break	ISO 527-2/5	3.0 %
Bending modulus	50.0mmSpan5	ASTM D790	4600 Mpa
Bending modulus	Bending modulus	--6	ISO 178	4600 Mpa
bending strength	--6,7	ISO 178	145 Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	145 Mpa
Tensile modulus	--3	ASTM D638	5000 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	5000 Mpa
tensile strength	Yield4	ASTM D638	88.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	220 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan10	ISO 75-2/Bf	224 °C
Vicat softening temperature	--	ASTMD152511	218 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	220 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	4.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7.4E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/5.0kg	ASTM D1238	18 g/10min
Melt Volume Flow Rate (MVR)	300°C/5.0kg	ISO 1133	15.0 cm3/10min
Shrinkage rate	MD:3.20mm	Internal Method	0.88-0.94 %
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	0.95-1.0 %
Water absorption rate	Saturation,23°C	ISO 62	3.8 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.50 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1E+16 ohms·cm
Dielectric strength	1.60mm,inAir	ASTM D149	23 KV/mm
Dielectric strength	Dielectric strength	1.60mm,inOil	ASTM D149	24 KV/mm
Compared to the anti leakage trace index	CTI	UL 746	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	V
High arc combustion index	HAI	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO/PA NORYL GTX™ GTX4610-1710 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet