Material Description
- Material Properties:High temperature creep resistance｜Dimensional stability
- Application Areas:Electronic field｜mechanical｜Bearing retainer
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 220 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 221 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 214 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 212 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 3.7E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 4.4E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 54 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.6 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：24小时 | ASTM D955 | 0.40-0.60 % |
| TD：24hr | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.51 % |
| 平衡,23°C,50%RH | ISO 62 | 0.85 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 4680 Mpa | |
| ISO 527-2/1 | 4420 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 105 Mpa |
| 屈服 | ISO 527-2/5 | 103 Mpa | |
| 断裂 | ASTM D638 | 102 Mpa | |
| 断裂 | ISO 527-2/5 | 102 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.4 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 4.3 % |
| elongation | 断裂 | ASTM D638 | 5.4 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 5.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 4370 Mpa |
| ISO 178 | 4060 Mpa | ||
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 176 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.