PC IUPILON™ GSH2010PH CB9501 MITSUBISHI ENGINEERING JAPAN

275

Unit Price:US$ 2,400 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
18MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜10%｜Filler by weight
Application Areas:Automotive Applications｜electrical equipment｜Phone
Color:--
Grade:Impact resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	90.0	Mpa
Bending modulus		ISO 178	2700	Mpa
Nominal tensile fracture strain		ISO 527-2	10	%
Tensile strain	Yield	ISO 527-2	5.0	%
tensile strength	Yield	ISO 527-2	52.0	Mpa
Tensile modulus		ISO 527-2	2900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	5.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	5.8E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	132	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	吸水率(Saturation,23°C)		0.14	%
	Shrinkage rate	MD:3.20mm		0.30-0.50	%
	Shrinkage rate	Shrinkage rate	TD:3.20mm		0.30-0.50	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	14.0	cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	15	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	CTI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC IUPILON™ GSH2010PH CB9501 MITSUBISHI ENGINEERING JAPAN

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index