ABS HI-121H LG YX NINGBO
1967
- Unit Price:US$ 1,245 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:786.7MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High gloss｜Thermal stability
- Application Areas:Air conditioner｜TV｜Automotive sector｜Washing machine｜Lighting fixtures
- Color:--
- Grade:Impact resistant grade
Material Certification
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | 5kg 50℃/nr | 103 °C | |
| Hot deformation temperature | 18.6kg/cm | ASTM D-259 | 93 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Whiteness | 青色反射率法 | 53 | |
| density | 23℃ | ASTM D-792 | 1.05 23℃ |
| melt mass-flow rate | 220℃ 10kg | ASTM D-1238 | 23 g/10min |
| Water absorption rate | 23℃ 24hr | ASTM D-570 | 0.3 % |
| Shrinkage rate | ASTM D-955 | 0.3-0.5 % | |
| Combustibility | all color | UL -94 | HB |
| gloss | 45° | 104 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | 50mm/min | ASTM D-638 | 18 % |
| Bending modulus | 5mm/min | ASTM D-790 | 26000 kg/cm |
| Impact strength of cantilever beam gap | 1/4〃 Notched | ASTM D-256 | 22 kg.cm/cm |
| Rockwell hardness | ASTM D-785 | 109 R | |
| bending strength | 5mm/min | ASTM D-790 | 800 kg/cm |
| tensile strength | 50mm/min | ASTM D-638 | 500 kg/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.