PP SABIC® G3230A-10000 SABIC INNOVATIVE US

344

Unit Price:US$ 3,000 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Homopolymer｜Glass fiber reinforced
Application Areas:Engine hood parts
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Gardner Impact	23°C	ASTM D5420	0.520	J
InstrumentedDartImpact	23°C,EnergyatPeakLoad	ASTM D3763	7.65	J
Suspended wall beam without notch impact strength	23°C,3.20mm	ASTM D4812	570	J/m
Impact strength of cantilever beam gap	23°C	ISO 180/1A	10	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	81	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	50.0mmSpan5	ISO 178	6600	Mpa
Bending modulus	Bending modulus	50.0mmSpan4	ASTM D790	5130	Mpa
Tensile strain	Break	ISO 527-2/50	3.3	%
elongation	Break	ASTM D638	2.7	%
tensile strength	Break	ISO 527-2/1A/50	85.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	83.0	Mpa
Tensile modulus		ISO 527-2/1	6500	Mpa
Tensile modulus	Tensile modulus		ASTM D638	6590	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-30to100°C	ISO 11359-2	1.6E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-30to100°C	ISO 11359-2	5.6E-06	cm/cm/°C
Vicat softening temperature		ISO 306/A50	164	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	150	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	150	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	159	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD:23°C,48hr	Internal Method	0.40	%
Shrinkage rate	Shrinkage rate	TD:23°C,48hr	Internal Method	0.70	%
melt mass-flow rate	230°C/2.16kg	ISO 1133	12	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Guangzhou HuShang Chemical	US$ 3000 /MT
Dongguan Boxin Plastic	US$ 3130 /MT

Supplier Join

Get App

Top

PP SABIC® G3230A-10000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index