ABS CYCOLAC™ FR23 BK4051 SABIC INNOVATIVE US

301

Unit Price:US$ 4,700 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High mobility｜Good flexibility
Application Areas:--
Color:--
Grade:Extrusion grade

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	200°C, 1000 sec^-1	ASTM D3835	310	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	41.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.5 mm	UL 94	5VB
UL flame retardant rating	UL flame retardant rating	2.3 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span	ASTM D790	73.0	Mpa
Bending modulus	50.0 mm Span	ASTM D790	2720	Mpa
elongation	Break	ASTM D638	11	%
elongation	elongation	Yield	ASTM D638	2.1	%
tensile strength	Break	ASTM D638	35.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	42.0	Mpa
Tensile modulus		ASTM D638	2410	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying time			2.0 to 4.0	hr
drying temperature			80 to 90	°C
Suggested maximum moisture content			0.10	%
Suggested injection volume			50 to 70	%
Temperature at the rear of the barrel			170 to 180	°C
Temperature in the middle of the barrel			195 to 205	°C
Temperature at the front of the material cylinder			200 to 215	°C
Spray nozzle temperature			200 to 220	°C
Processing (melt) temperature			200 to 220	°C
Mold temperature			50 to 70	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			30 to 60	rpm
Exhaust hole depth			0.038 to 0.051	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
RTI Elec		UL 746	60.0	°C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.9E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.9E-5	cm/cm/°C
Vicat softening temperature		ASTM D15255	90.0	°C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	72.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	83.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Melt Volume Flow Rate (MVR)	220°C/10.0 kg	ISO 1133	37.0	cm3/10min
melt mass-flow rate	220°C/5.0 kg	ISO 1133	9.0	g/10 min
melt mass-flow rate	melt mass-flow rate	230°C/3.8 kg	ASTM D1238	6.8	g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ABS CYCOLAC™ FR23 BK4051 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index