PBT

PBT Cristin® SK641FR-BK851 DUPONT USA

169

Unit Price:US$ 4,283 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜15% filler by weight
Application Areas:Automotive Applications｜Electronic and electrical components
Color:--
Grade:Flame retardant enhanced grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	33 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	32 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	53 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	44 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	V-0
UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-0
Extreme Oxygen Index		ISO 4589-2	31 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2	100 Mpa
Tensile strain	Break	ISO 527-2	3.4 %
Tensile modulus		ISO 527-2	7200 Mpa
Tensile creep modulus	1hr	ISO 899-1	6000 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	4800 Mpa
bending strength		ISO 178	155 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	5E-05 cm/cm/°C
Melting temperature		ISO 11357-3	225 °C
Vicat softening temperature		ISO 306/B50	207 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	203 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	218 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.14 %
Water absorption rate	Water absorption rate	23°C,24hr,2.00mm	ISO 62	0.33 %
Shrinkage rate	MD2	ISO 294-4	0.80 %
	Shrinkage rate	MD	ISO 294-4	0.70 %
		Shrinkage rate	TD	ISO 294-4	1.2 %
		Shrinkage rate	Shrinkage rate	TD2	ISO 294-4	1.5 %
MediumDensity			1.37 g/cm³
SpecificHeatCapacity of Melt			1740 J/kg/°C
ThermalConductivityofMelt			0.27 W/m/K

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1MHz	IEC 60250	0.017
Dissipation factor	Dissipation factor	100Hz	IEC 60250	3E-03
Relative permittivity	1MHz	IEC 60250	3.50
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.70
Dielectric strength		IEC 60243-1	28 KV/mm
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Surface resistivity		IEC 60093	1E+15 ohms
Compared to the anti leakage trace index		IEC 60112	V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.