POM

POM CELCON® GB25 CELANESE USA

285

Unit Price:US$ 3,049 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
108.7MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Bending resistance｜Low contractility｜Filler: Glass beads｜25% filler by weight
Application Areas:Automotive Applications｜pipeline｜Thin walled components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	2.2 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	2.6 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	2.4 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178	3600 Mpa
Tensile strain	Yield	ISO 527-2/1A/50	4.0 %
tensile strength	Yield	ISO 527-2/1A/50	49.0 Mpa
	tensile strength	Yield,82°C	ASTM D638	26.2 Mpa
		tensile strength	Yield,23°C	ASTM D638	46.2 Mpa
		tensile strength	tensile strength	Yield,-40°C	ASTM D638	73.1 Mpa
Tensile modulus		ISO 527-2/1A/1	3700 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Melting temperature		ISO 11357-3	165 °C
Melting temperature	Melting temperature		ASTM D3418	166 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	105 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	118 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ISO 294-4	1.5 %
	Shrinkage rate	TD	ISO 294-4	1.3 %
		Shrinkage rate	TD	ASTM D955	1.4 %
		Shrinkage rate	Shrinkage rate	MD	ASTM D955	1.6 %
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	13.0 cm3/10min
density		ISO 1183	1.58 g/cm³
density	density		ASTM D792	1.62 g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.65 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.