Material Properties:High temperature resistance｜Glass fiber reinforced｜Filler: Glass mineral｜60% filler by weight
Application Areas:Casters｜Electrical applications｜sporting goods
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		内部方法	0.71 %
Shrinkage rate	Shrinkage rate		内部方法	0.22 %
Water absorption rate		ISO 62	0.020 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	122

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

Supplementary Information	Test Condition	Test Method	Test Result
BarFlowLength		内部方法	135 mm

Mechanical properties	Test Method	Test Result
tensile strength	ISO 527-2	140 Mpa
Tensile strain	ISO 527-2	0.90 %
Flexural modulus	ISO 178	19000 Mpa
bending strength	ISO 178	220 Mpa
shear strength	JISK7214	60.0 Mpa
coefficient of friction		0.28
Taber abraser	ISO 9352	70.0 mg

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	19 kJ/m²

Electrical performance	Test Method	Test Result
Volume resistivity	IEC 60093	1E+16 ohms·cm
dielectric strength	IEC 60243-1	24 KV/mm
dielectric constant	IEC 60250	4.90
Dissipation Factor	IEC 60250	2E-03

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	260 °C
melting temperature		ISO 11357-3	278 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	2.8E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.