PC LEXAN™ 925AU SABIC INNOVATIVE US
226
- Unit Price:US$ 2,788 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:72.6MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Bromine free｜currency
- Application Areas:Plastic bag｜Lighting applications｜Electrical field｜Electronic field｜Architectural application field｜Electrical appliances｜lens
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D15255 | 143 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 7.4E-05 cm/cm/°C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 137 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 126 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-2 |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 800 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 79.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 2 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.19 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 13 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.60-0.80 % |
| Outdoor applicability | UL 746C | f1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2270 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 断裂 | ASTM D638 | 67.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| 断裂 | ASTM D638 | 130 % | |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2370 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 101 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.