POM CELCON® M25NAT CELANESE USA

Unit Price:US$ 2,810 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Caihua Plastic Technology Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high viscosity｜wear resistant｜High sliding｜enhance
Application Areas:Household appliances｜Household appliances｜Fitness equipment｜Automotive sector｜Electric wire｜Cable
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	190	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C,Partial Break	ISO 179/1eU	250	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23°C	ISO 178	2430	Mpa
Tensile creep modulus	1000hr	ISO 899-1	1100	Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	2100	Mpa
tensile strength	Yield,23°C	ASTM D638	60.7	Mpa
tensile strength	tensile strength	Yield,-40°C	ASTM D638	94.5	Mpa
Tensile modulus		ISO 527-2/1A/1	2460	Mpa
Tensile strain	Yield	ISO 527-2/1A/50	12	%
tensile strength	Yield	ISO 527-2/1A/50	63.0	Mpa
tensile strength	tensile strength	Yield,71°C	ASTM D638	34.5	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-04	cm/cm/°C
Melting temperature		ISO 11357-3	166	°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	94.0	°C
Melting temperature		ASTM D3418	165	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Density of Melt		Internal Method	1.200	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.75	%
Shrinkage rate	MD	ISO 294-4	2.2	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.8	%
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	2.20	cm3/10min
melt mass-flow rate		ASTM D1238	2.5	g/10min
Shrinkage rate	TD	ASTM D955	1.8	%
Shrinkage rate	Shrinkage rate	MD	ASTM D955	2.2	%
ThermalConductivityofMelt		Internal Method	0.16	W/m/K
SpecificHeatCapacity of Melt		Internal Method	2210	J/kg/°C
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1E+14	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 2800 /MT

Supplier Join

Get App

Top

POM CELCON® M25NAT CELANESE USA

Material Description

Technical Data Sheet