PC/PBT XENOY™ X2420 BK1066 SABIC INNOVATIVE NANSHA
195
- Unit Price:US$ 4,395 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:53MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High impact resistance｜Dimensional stability｜Filler: Glass fiber reinforced material｜10% filler by weight
- Application Areas:Automotive Applications
- Color:--
- Grade:Chemical resistance
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 111 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 101 °C | |
| vicat | ISO 306/B120 | 118 °C | |
| Flow: -40 to 40 ° C | ASTME831 | 5E-05 cm/cm/°C | |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 4E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 8E-05 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 9E-05 cm/cm/°C |
| RTI Elec | UL 746 | 75.0 °C | |
| RTI Imp | UL 746 | 75.0 °C | |
| RTI | UL 746 | 75.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.400mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| 23°C | ISO 179/1eA | 15 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 95 kJ/m² |
| 23°C | ISO 179/1eU | 95 kJ/m² | |
| 23°C | ASTM D256 | 210 J/m | |
| -30°C | ISO 180/1A | 8.0 kJ/m² | |
| 23°C | ISO 180/1A | 14 kJ/m² | |
| ASTM D4812 | 1600 J/m | ||
| -30°C | ISO 180/1U | 74 kJ/m² | |
| 23°C | ISO 180/1U | 110 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 36.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| 300°C/1.2kg | ISO 1133 | 26.0 cm3/10min | |
| shrinkage rate | MD:3.20mm | 内部方法 | 0.15-0.25 % |
| TD:3.20mm | 内部方法 | 0.30-0.40 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.020 % |
| 平衡,23°C,50%RH | ISO 62 | 0.040 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3800 Mpa | |
| yield | ASTM D638 | 50.0 Mpa | |
| ISO 527-2/5 | 51.0 Mpa | ||
| fracture | ASTM D638 | 35.0 Mpa | |
| ISO 527-2/5 | 37.0 Mpa | ||
| yield | ASTM D638 | 3.0 % | |
| ISO 527-2/5 | 3.0 % | ||
| fracture | ISO 527-2/5 | 7.0 % | |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 3500 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 90.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.