Material Description

Material Properties:High mobility｜Thermal stability｜Antistatic｜Weather resistance
Application Areas:Automotive sector
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	60°, 无织构	ASTM D523	94

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	47.0 J
Dart impact	Dart impact	-30°C, Total Energy	ASTM D3763	30.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span3	ASTM D790	88.0 Mpa
bending strength	bending strength	--4,5	ISO 178	75.0 Mpa
Bending modulus	--4	ISO 178	2500 Mpa
Bending modulus	Bending modulus	50.0 mm Span3	ASTM D790	2510 Mpa
Tensile strain	Break	ISO 527-2/50	130 %
	Tensile strain	Break2	ASTM D638	25 %
	Tensile strain	Tensile strain	Yield	ISO 527-2/50	4.5 %
tensile strength	Break	ISO 527-2/50	50.0 Mpa
	tensile strength	Yield	ISO 527-2/50	57.0 Mpa
	tensile strength	tensile strength	Yield2	ASTM D638	62.0 Mpa
Tensile modulus		ISO 527-2/1	2500 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			95 to 105 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.040 %
Suggested injection volume			40 to 80 %
Temperature at the rear of the barrel			240 to 255 °C
Temperature in the middle of the barrel			245 to 260 °C
Temperature at the front of the material cylinder			250 to 265 °C
Spray nozzle temperature			245 to 265 °C
Processing (melt) temperature			260 to 275 °C
Mold temperature			55 to 70 °C
Back pressure			0.300 to 1.00 Mpa
Screw speed			30 to 80 rpm
Exhaust hole depth			0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	98.0 °C
Vicat softening temperature		ISO 306/B50	113 °C
Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	104 °C
Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
thermal conductivity		ASTM C177	0.25 W/m/K
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Bf	116 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f2
Water absorption rate	24 hr	ASTM D570	0.25 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
melt mass-flow rate	280°C/3.8 kg	ASTM D1238	24 g/10 min
	melt mass-flow rate	260°C/5.0 kg	ASTM D1238	14 g/10 min
	melt mass-flow rate	melt mass-flow rate	220°C/10.0 kg	ASTM D1238	5.0 g/10 min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ASA/PC GELOY™ XP4034-NA1000 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet