Material Properties:Flame retardant｜High rigidity｜Bromine free｜Filler: Mineral filler
Application Areas:Industrial applications｜Business equipment｜Business equipment｜Industrial applications
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	120 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	108 °C
vicat		ISO 306/B50	122 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	3.7E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	2.0mm	UL 94	5VB

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	18 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	1E+16 ohms

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	TD:4.00mm	内部方法	0.20-0.40 %
shrinkage rate	shrinkage rate	MD:4.00mm	内部方法	0.10-0.30 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	9000 Mpa
tensile strength	断裂	ISO 527-2/5	66.0 Mpa
Tensile strain	断裂	ISO 527-2/5	2.0 %
flexural modulus		ISO 178	8000 Mpa
bending strength		ISO 178	100 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.