'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS FORTRON® 1140L6 SF3001 CELANESE USA
5
- Unit Price:US$ 8,180 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Dongguan Chaoren Plastic Raw Materials Co., Ltd
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜High temperature resistance
- Application Areas:fibre｜Bottle cap
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 10 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 10 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 53 | kJ/m² |
| 23°C | ISO 179/1eU | 53 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.38mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | ISO 62 | 0.02 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | ISO 178 | 14500 | Mpa | |
| bending strength | ISO 178 | 285 | Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 10 | kJ/m² |
| Rockwell hardness | ISO 2039-2 | 100 | M-scale | |
| Tensile modulus | ISO 527-2/1A/1 | 14700 | Mpa | |
| elongation | Break | ISO 527-1 | 1.9 | % |
| tensile strength | ISO 527-1 | 195 | Mpa | |
| Tensile modulus | ISO 527-1 | 14700 | Mpa | |
| bending strength | ISO 178 | 285 | Mpa | |
| tensile strength | Break,23°C | ASTM D638 | 200 | Mpa |
| Break | ISO 527-2/1A/5 | 195 | Mpa | |
| elongation | Break,23°C | ASTM D638 | 2.0 | % |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.9 | % |
| Bending modulus | 23°C | ISO 178 | 14500 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 4.2E-05 | cm/cm/°C |
| MD | ISO 11359-2 | 2.6E-05 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| UL flame retardant rating | UL 94 | V-0 | ||
| Hot deformation temperature | 1.80Mpa | ISO 75-1 | 270 | °C |
| 0.45MPa,Annealed | ASTM D648 | 280 | °C | |
| 1.8MPa,Unannealed | ASTM D648 | 265 | °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 270 | °C | |
| 8.0MPa,Unannealed | ISO 75-2/C | 215 | °C | |
| Glass transition temperature | ISO 11357-2 | 90.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.020 | % |
| Spiral flow length | Internal Method | 21.5 | ||
| Shrinkage rate | MD | ISO 294-4 | 0.20-0.60 | % |
| TD | ISO 294-4 | 0.40-0.60 | % | |
| TD | ASTM D955 | 0.50-0.70 | % | |
| MD | ASTM D955 | 0.20-0.30 | % | |
| melt mass-flow rate | ASTM D1238 | 19 | g/10min | |
| density | ISO 1183 | 1.65 | g/cm³ | |
| Specific volume | ASTM D792 | 0.625 | cm³/g | |
| Shrinkage rate | ISO 2577 | 0.2-0.6 | % | |
| density | ISO 1183 | 1.65 | g/cm³ | |
| ASTM D792 | 1.60 | g/cm³ | ||
| SpecificHeatCapacity of Melt | Internal Method | 1500 | J/kg/°C | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dielectric constant | 1MHz | ASTM D150 | 3.50 | |
| 1kHz | ASTM D150 | 3.50 | ||
| Dielectric strength | IEC 60243-1 | 28 | KV/mm | |
| ASTM D149 | 15 | KV/mm | ||
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| ASTM D257 | 1E+16 | ohms·cm | ||
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Relative permittivity | 1MHz | IEC 60250 | 4.10 | |
| Dissipation factor | 1kHz | ASTM D150 | 1E-03 | |
| 1MHz | ASTM D150 | 1E-03 | ||
| 1MHz | IEC 60250 | 2E-03 | ||
| Arc resistance | ASTM D495 | 134 | sec | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 4 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ASTM D785 | 100 | |
| M-Scale | ISO 2039-2 | 100 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| CSARating | 8.40E-7mm | CSAF-1 | A00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.