MVLDPE

MVLDPE DOWLEX™  2045.11G STYRON US

272
  • Unit Price:US$ 1,342 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    12MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
gloss45°ASTM D245734
turbidityASTM D100320 %
gloss45°，20.3umASTM D-245770
gloss45°，50.8umASTM D-245767
turbidity20.3umASTM D-10037 %
turbidity50.8umASTM D-100310 %
Other performanceTest ConditionTest MethodTest Result
Film toughness20.3um，TDASTM D-882304 J/cm³
Film toughness20.3um，MDASTM D-882240 J/cm4
Film toughness50.8um，MDASTM D-882273 J/cm5
Film toughness50.8um，TDASTM D-882292 J/cm6
Thin film puncture strength20.3umInternal Method11.4 J/cm³
Thin film puncture strength50.8umInternal Method9.76 J/cm³
machinabilityTest ConditionTest MethodTest Result
Melt Temperature221-232 °C
Basic PerformanceTest ConditionTest MethodTest Result
melt mass-flow rate190℃/2.16kgASTM D-12381 g/10min
densityASTM D-7920.922 g/m3
mechanical propertiesTest ConditionTest MethodTest Result
Elmendorf tear strength50.8um，MDASTM D-1922740 g
Elmendorf tear strength50.8um，TDASTM D-19221200 g
Elmendorf tear strength20.3um，MDASTM D-1922440 g
Elongation at Break50.8um，TDASTM D-882770 %
Elongation at Break20.3um，TDASTM D-882750 %
Elongation at Break20.3um，MDASTM D-882480 %
tensile strength50.8um，TD,BreakASTM D-88244.3 Mpa
tensile strength50.8um，MD,BreakASTM D-88251.9 Mpa
tensile strength20.3um，TD,BreakASTM D-88249.2 Mpa
tensile strength20.3um，MD,BreakASTM D-88260.4 Mpa
tensile strength50.8um，Yield,TDASTM D-88212.6 Mpa
tensile strength50.8um，Yield,MDASTM D-88211.8 Mpa
tensile strength20.3um，Yield,MDASTM D-88212.7 Mpa
tensile strength20.3um，Yield,TDASTM D-88213.1 Mpa
Secant modulus2% Secant，50.8um，TDASTM D-882234 Mpa
Secant modulus2% Secant，50.8um，MDASTM D-882196 Mpa
Secant modulus20.3um，TDASTM D-882247 Mpa
Secant modulus20.3um，MDASTM D-882227 Mpa
Elmendorf tear strength20.3um，TDASTM D-1922580 g
Dart impact50.8umASTM D-1709A280 g
Dart impact20.3umASTM D-1709A130 g
Elongation at Break50.8um，MDASTM D-882670 %
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperatureASTM D-1525104 °C
Melting temperatureInternal Method122 °C
Melting temperatureInternal Method122 °C
Vicat softening temperatureASTM D1525104 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate190°C/2.16kgASTM D12381.0 g/10min
filmTest ConditionTest MethodTest Result
tensile strengthMD:BreakASTM D88246.1 Mpa
tensile strengthTD:BreakASTM D88235.3 Mpa
elongationMD:BreakASTM D882540 %
elongationTD:BreakASTM D882660 %
Secant modulus1%Secant,TDASTM D882234 Mpa
Secant modulus2%Secant,TDASTM D882189 Mpa
tensile strengthMD:YieldASTM D88213.4 Mpa
tensile strengthTD:YieldASTM D88214.1 Mpa
film thicknessInternal Method25 µm
Thin film puncture strengthInternal Method1.24 J
Thin film puncture strengthInternal Method31.1 N
Thin film puncture strengthInternal Method6.21 J/cm³
Membrane strengthMDASTM D882110 J/cm³
Membrane strengthTDASTM D882114 J/cm³
Secant modulus1%Secant,MDASTM D882211 Mpa
Secant modulus2%Secant,MDASTM D882172 Mpa
Dart impactASTM D1709A180 g
Elmendorf tear strengthMDASTM D1922440 g
Elmendorf tear strengthTDASTM D1922630 g
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.