PPO/PA

PPO/PA NORYL GTX™ GTX900-74701 SABIC INNOVATIVE US

346

Unit Price:US$ 4,241 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
65MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High temperature resistance
Application Areas:For external use in automobiles
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--3	ASTM D638	2300 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400 Mpa
tensile strength	Yield4	ASTM D638	65.0 Mpa
	tensile strength	Yield	ISO 527-2/50	65.0 Mpa
		tensile strength	Break4	ASTM D638	55.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0 Mpa
elongation	Yield4	ASTM D638	5.0 %
	elongation	Yield	ISO 527-2/50	4.5 %
		elongation	Break4	ASTM D638	60 %
		elongation	elongation	Break	ISO 527-2/50	25 %
Bending modulus	50.0mmSpan5	ASTM D790	2350 Mpa
Bending modulus	Bending modulus	--6	ISO 178	2200 Mpa
bending strength	--6,7	ISO 178	90.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	95.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7E-05 cm/cm/°C
thermal conductivity		ISO 8302	0.23 W/m/K
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	190 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan10	ISO 75-2/Be	190 °C
Vicat softening temperature	--	ASTM D-596	205 °C
	Vicat softening temperature	--	ISO 306/A50	250 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	200 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:3.20mm	Internal Method	1.1-1.4 %
Water absorption rate	Saturation,23°C	ISO 62	3.5 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2 %
melt mass-flow rate	280°C/5.0kg	ASTM D1238	13 g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	13.0 cm3/10min
Shrinkage rate	MD2	Internal Method	1.6-2.0 %
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	1.4-1.7 %

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H358/30	ISO 2039-1	85.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO/PA NORYL GTX™ GTX900-74701 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet