PP LATENE® 22H2 MX/25 LATI ITALY
123
- Unit Price:US$ 1,650 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:21MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Filler: Mineral filler｜25% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 1.25 % | |
| ISO 294-4 | 1.35 % |
| Flame retardancy | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 25 Mpa | |
| elongation at break | ISO 527-2 | 6.00 % | |
| Tensile modulus | ISO 527-2 | 2600 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 3.50 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 105 °C | |
| ISO 75-2/Af | 55 °C | ||
| vicat | ISO 306/B50 | 95 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.