Material Description

Material Properties:Low extract｜Easy to form｜Easy to demould
Application Areas:Plastic bag｜Medical and nursing supplies
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C6	ISO 180/1U	58 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	910 J/m

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break, 50.0 mm Span	ASTM D790	149 Mpa
Bending modulus	--5	ISO 178	7860 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	8230 Mpa
elongation	Break	ISO 527-2/5	7.5 %
	elongation	Break3	ASTM D638	3.2 %
	elongation	elongation	Yield3	ASTM D638	2.7 %
tensile strength	Break	ISO 527-2/5	114 Mpa
tensile strength	tensile strength	Break3	ASTM D638	114 Mpa
Tensile modulus		ASTM D638	8630 Mpa

injection	Test Condition	Test Method	Test Result
Mold temperature			80 to 110 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm
Processing (melt) temperature			305 to 325 °C
Temperature at the front of the material cylinder			320 to 330 °C
Temperature in the middle of the barrel			310 to 320 °C
Temperature at the rear of the barrel			295 to 305 °C
Suggested maximum moisture content			0.020 %
drying time			4.0 hr
drying temperature			120 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Af	142 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	140 °C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span6	ISO 75-2/Bf	146 °C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	144 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.070 %
Water absorption rate	Water absorption rate	24 hr, 50% RH	ASTM D570	0.070 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.