PET Rynite® FR515 BK507 DUPONT SHENZHEN
215
- Unit Price:US$ 4,975 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜enhance｜Filler: Glass fiber reinforced material｜15% filler by weight
- Application Areas:Electrical enclosure｜Electrical field｜Electronic field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 88 |
| R计秤 | ISO 2039-2 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 200 °C |
| vicat | ISO 306/B50 | 210 °C | |
| melting temperature | ISO 11357-3 | 254 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 3.3E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1.2E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 8.8E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 240 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| UL flame retardant rating | 0.9mm | UL 94 | V-0 |
| 1.5mm | UL 94 | 5VA | |
| 0.9mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | 5VA | |
| Limiting Oxygen Index | ISO 4589-2 | 32 % | |
| FMVSS flammability | FMVSS302 | B |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| 1MHz | IEC 60250 | 3.50 | |
| Dissipation Factor | 100Hz | IEC 60250 | 9E-03 |
| 1MHz | IEC 60250 | 0.015 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| IEC 60112 | V | ||
| surface resistivity | IEC 60093 | 1E+13 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 170 °C | ||
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 6.00 cm3/10min |
| shrinkage rate | TD2 | ISO 294-4 | 1.2 % |
| TD | ISO 294-4 | 0.80 % | |
| MD | ISO 294-4 | 0.30 % | |
| MD2 | ISO 294-4 | 0.50 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 170 Mpa | |
| tensile modulus | ISO 527-2 | 6800 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 107 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
| flexural modulus | ISO 178 | 5940 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 20 kJ/m² |
| -30°C | ISO 179/1eU | 35 kJ/m² | |
| 23°C | ISO 179/1eU | 40 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.