TPEE DYM100 NC010 DUPONT BELGIUM

249
  • Unit Price:US$ 6,805 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High impact｜Medium rigidity
  • Application Areas:engineering application ｜Automotive components
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU430 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
flammabilityTest ConditionTest MethodTest Result
AtomizationG-value(condensate)ISO 64521E-04 g
AtomizationF-value(refraction)ISO 645291 %
UL flame retardant rating0.8mmUL 94HB
Burning rate1.00mmISO 379530 mm/min
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating0.8mmIEC 60695-11-10,-20HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
mechanical propertiesTest ConditionTest MethodTest Result
Tensile creep modulus1hrISO 899-12900 Mpa
Nominal tensile fracture strainISO 527-245 %
Tensile strainYieldISO 527-226 %
tensile strengthYieldISO 527-272.0 Mpa
Tensile modulusISO 527-23000 Mpa
Tensile creep modulus1000hrISO 899-11600 Mpa
Bending modulusISO 1782900 Mpa
bending strength3.5%StrainISO 17879.0 Mpa
Compressive stressISO 604110 Mpa
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionTD：EffectiveThermalDiffusivityISO 11359-21E-07 m²/s
Linear coefficient of thermal expansionTD：AnnealingTime-OptionalISO 11359-230.0 min/mm
Linear coefficient of thermal expansionTD：AnnealingTemperatureISO 11359-2160 °C
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-21E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：--ISO 11359-21.1E-04 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-21E-04 cm/cm/°C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B160 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A100 °C
Vicat softening temperature--ISO 306/A50175 °C
Vicat softening temperature--ISO 306/B50160 °C
Melting temperatureISO 11357-3178 °C
Linear coefficient of thermal expansionMD：--ISO 11359-21.1E-04 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateSaturation,23°C,2.00mmISO 620.90 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.20 %
Shrinkage rateMDISO 294-42.2 %
Shrinkage rateTDISO 294-41.8 %
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 11331.90 cm3/10min
melt mass-flow rateISO 11332.3 g/10min
SpecificHeatCapacity of Melt3000 J/kg/°C
MediumDensity1.19 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Relative permittivity100HzIEC 602503.90
Dielectric strengthIEC 60243-141 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Surface resistivityIEC 600933E+13 ohms
Relative permittivity1MHzIEC 602503.80
Dissipation factor100HzIEC 602501E-03
Dissipation factor1MHzIEC 602505.5E-03
Compared to the anti leakage trace indexIEC 60112 V
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM-SaleISO 2039-290
Rockwell hardnessR-SaleISO 2039-2121
Supplementary InformationTest ConditionTest MethodTest Result
EmissionofOrganicCompoundsVDA2774.00 µgC/g
EmissionVDA275<8.00 mg/kg
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.