PC LEXAN™ XHT4141-RD3G066 SABIC INNOVATIVE NANSHA

Unit Price:US$ 7,520 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Guangyan Plastic Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜transparent｜High temperature resistance
Application Areas:Casters｜Sports Equipment
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	72.0	J
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	HB
Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875	°C
Metallic haze	起始	Internal Method	175	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--	ISO 527-2/1	2750	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2730	Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	120	Mpa
bending strength	bending strength	--5,6	ISO 178	80.0	Mpa
Bending modulus	--5	ISO 178	2600	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2600	Mpa
elongation	Break	ISO 527-2/50	50	%
	elongation	Break3	ASTM D638	50	%
		elongation	Yield	ISO 527-2/50	7.0	%
		elongation	elongation	Yield3	ASTM D638	7.0	%
tensile strength	Break	ISO 527-2/50	67.0	Mpa
	tensile strength	Break3	ASTM D638	69.0	Mpa
		tensile strength	Yield	ISO 527-2/50	78.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	77.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature at the front of the material cylinder			300 to 345	°C
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			280 to 325	°C
Spray nozzle temperature			295 to 340	°C
Processing (melt) temperature			300 to 345	°C
Mold temperature			95 to 130	°C
drying temperature			135	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.020	%
Temperature in the middle of the barrel			290 to 335	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 90	rpm
Exhaust hole depth			0.025 to 0.080	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	174	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Bf	173	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	165	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	162	°C
Vicat softening temperature	--	ASTM D152510	183	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	181	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	163 to 167°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.0E-5	cm/cm/°C
thermal conductivity	25°C	ASTM C177	0.20	W/m/K
RTI Elec		UL 746	150	°C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.0E-5	cm/cm/°C
RTI Imp		UL 746	130	°C
RTI		UL 746	150	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.25	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.50	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.95	%
Melt Volume Flow Rate (MVR)	330°C/2.16 kg	ISO 1133	24.0	cm3/10min
melt mass-flow rate	330°C/2.16 kg	ASTM D1238	25	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	100 Hz	ASTM D150	3.12
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.02
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3
Surface resistivity		ASTM D257	> 1.0E+17	ohms
Volume resistivity		ASTM D257	> 1.0E+17	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 5280 /MT

Supplier Join

Get App

Top

PC LEXAN™ XHT4141-RD3G066 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index