PSU

PSU Ultrason®S S2010G4 BASF GERMANY

319

Unit Price:US$ 23,031 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜wear resistant｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Food containers｜Medical equipment｜Printing machine parts
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	170 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Imp	1.6mm	UL 746	140 °C
RTI Imp	RTI Imp	3.0mm	UL 746	140 °C
RTI Str	1.6mm	UL 746	160 °C
RTI Str	RTI Str	3.0mm	UL 746	160 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	184 °C
Linear coefficient of thermal expansion	MD		2.6E-05 cm/cm/°C
RTI Elec	1.6mm	UL 746	160 °C
RTI Elec	RTI Elec	3.0mm	UL 746	160 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+13 ohms·cm
Dielectric strength		IEC 60243-1	46 KV/mm
Dielectric constant	100Hz	IEC 60250	3.50
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3.50
Dissipation factor	100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	6E-03
Compared to the anti leakage trace index		IEC 60112	PLC 4

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.38 g/cm³
Melt Volume Flow Rate (MVR)	360°C/10.0kg	ISO 1133	40.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	0.52 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.31 %
Water absorption rate	Saturation,23°C	ISO 62	0.70 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	6600 Mpa
tensile strength	Break,23°C	ISO 527-2	115 Mpa
Tensile strain	Break,23°C	ISO 527-2	2.9 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	8.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	55 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	50 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	8.0 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PSU Ultrason®S S2010G4 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet