POM Delrin® 500 BK DUPONT USA

200

Unit Price:US$ 3,335 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
161.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜High impact resistance｜Thermal stability
Application Areas:Automotive Applications｜Fitness equipment｜Engine parts
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M计秤	ISO 2039-2	92
Rockwell hardness	Rockwell hardness	R计秤	ISO 2039-2	120

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	158 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	90.0 °C
vicat		ISO 306/B50	160 °C
melting temperature		ISO 11357-3	178 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04 cm/cm/°C
AnnealingTemperature			160 °C
AnnealingTime-Optional			30.0 min/mm

flammability	Test Condition	Test Method	Test Result
burning rate	1.00mm	ISO 3795	28 mm/min
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B

Supplementary Information	Test Condition	Test Method	Test Result
Emissions of Organic Compounds		VDA277	6.00 µgC/g
Emission		VDA275	<8.00 mg/kg

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	290 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	350 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	9.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.0 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	>1.0E+15 ohms
relative permittivity	100Hz	IEC 60250	4.20
relative permittivity	relative permittivity	1MHz	IEC 60250	4.10
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.41 g/cm³
melt mass-flow rate		ISO 1133	15 g/10min
Melt volume flow rate	190°C/2.16kg	ISO 1133	12.0 cm3/10min
shrinkage rate	TD	ISO 294-4	1.8 %
shrinkage rate	shrinkage rate	MD	ISO 294-4	1.9 %
Water absorption rate	饱和,23°C,2.00mm	ISO 62	1.0 %
Water absorption rate	Water absorption rate	平衡,23°C,2.00mm,50%RH	ISO 62	0.25 %

mechanical properties	Test Condition	Test Method	Test Result
Nominal tensile fracture strain		ISO 527-2	25 %
flexural modulus		ISO 178	2900 Mpa
Tensile modulus		ISO 527-2	3100 Mpa
tensile strength	屈服	ISO 527-2	67.0 Mpa
Tensile strain	屈服	ISO 527-2	15 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.