PPO NORYL™ SE1GFN1-701 SABIC INNOVATIVE SHANGHAI
319
- Unit Price:US$ 4,754 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:58MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:enhance｜Glass fiber reinforced｜Flame retardant｜High mobility｜High temperature resistance
- Application Areas:Electronic communication accessories｜Electronic communication accessories｜Household appliances｜Household appliances｜Automotive interior parts｜Sports Equipment｜Above water
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.30 - 0.50 % | |
| Water absorption rate | ASTM D570 | 0.070 % | |
| ASTM D570 | 0.22 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 104 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-1 | |
| Limiting Oxygen Index | ASTM D2863 | 34 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 74.0 Mpa | |
| elongation | ASTM D638 | 5.0 % | |
| Flexural modulus | ASTM D790 | 3990 Mpa | |
| bending strength | ASTM D790 | 119 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | ASTM D150 | 3.00 | |
| ASTM D150 | 3.00 | ||
| ASTM D150 | 3.00 | ||
| Dissipation Factor | ASTM D150 | 1.7E-3 | |
| ASTM D150 | 1.7E-3 | ||
| ASTM D150 | 1.6E-3 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 2 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 1 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 105 to 110 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 250 to 300 °C | ||
| Temperature in the middle of the barrel | 260 to 305 °C | ||
| Temperature at the front of the material cylinder | 270 to 310 °C | ||
| Spray nozzle temperature | 280 to 310 °C | ||
| Processing (melt) temperature | 280 to 310 °C | ||
| Temperature | 75 to 105 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 20 to 100 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 131 °C | |
| vicat | ASTM D15254 | 147 °C | |
| RTI Elec | UL 746 | 110 °C | |
| RTI Imp | UL 746 | 105 °C | |
| RTI | UL 746 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.