PVDF SOLEF® 20810-3 SOLVAY USA
265
- Unit Price:US$ 5,952 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity
- Application Areas:film｜adhesive
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 测试标准 | 数据 单位 | |
| ASTM D2240 | 60 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 退火，4.0mm | ASTM D648 | 62 °C |
| 退火，4.0mm | ASTM D648 | 40 °C | |
| vicat | 50°C/hr10N | ISO 306 | 120 °C |
| melting temperature | ASTM D3418 | 135 °C | |
| Glass Transition Temperature | -29 °C | ||
| brittle temperature | ASTM D746 | -22 °C | |
| thermal conductivity | JIS R2618 | 0.18 W/(m·K) | |
| specific heat | 1200 J/(kg·°C) | ||
| Specific heat capacity | 100℃ | 1600 J/(kg·°C) | |
| crystallization temperature | 92 | ||
| Average melting heat | 23 J/g | ||
| 24 J/g |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.78 g/cm³ | |
| shrinkage rate | 流动 | ASTM D995 | 2 % |
| ASTM D995 | 3 % | ||
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.04 % |
| melt mass-flow rate | ASTM D1238 | 2 g/10min | |
| ASTM D1238 | 6 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 100000000000000 Ω | |
| Limiting Oxygen Index | ASTM D2863 | 54.5 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C,1mm/min | ASTM D638 | 420 Mpa |
| tensile strength | 23°C,50mm/min | ASTM D638 | 40 Mpa |
| 屈服,23°C | ASTM D638 | 16.5 Mpa | |
| elongation | 23°C | ASTM D638 | 675 % |
| Elongation at break | 23°C,50mm/min | ASTM D638 | 13.5 % |
| bending strength | ASTM D790 | 40 Mpa | |
| flexural modulus | 23°C | ASTM D790 | 400 Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 180 J/m |
| coefficient of friction | 动态 | ASTM D3702 | 0.25 |
| 静态 | ASTM D3702 | 0.3 | |
| Taber wear resistance | 10 mg/1000cy |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.